Showing all 3 results
This PLA-based filament offers enhanced possibilities for industrial applications. The thermal stability of objects printed with Filaticum Engineering is extremely high, they could bear up to 120 °C heat, in most of the cases without any heat treatment after printing.
Filaticum Engineering is also much more resistant to other external impacts than standard PLA materials: it has a high tensile and compressive strength and extremely high stiffness, making it an excellent material for objects that are exposed to typical influences in industrial environments.
Filaticum Semiflex is a soft, flexible filament. Objects printed from this filament will not break or deform when they are moderately bent, and after that they will regain their original shape.
The filament has a Shore hardness value of 95, for comparison, it is equal to the hardness of a shopping trolley wheel, for example.
Filaticum Semiflex filament is already a flexible on the spool, easy to wind without breaking or stretching. It retains its softness after printing also, making it suitable for producing various types of catches, dampers and objects where it is important not to scratch other surfaces.
Thanks to its PLA base raw material, it is much easier to print than most other flexible filaments and does not require a special printer either.
Recommended printing settings: lower speed (50 mm/s) or higher temperature (215, max. 220 °C)
The strength, hardness, and heat resistance of filament reinforced with glass fiber go far beyond the characteristics of the standard PLA. It can withstand heat of up to 100 0C. The biopolymer-based filament is also suitable for printing lightweight parts, even applicable for replacing metal parts. The printed surface is unique, glassy, so it is also a perfect choice for designers. The warping of objects printed with Filaticum Glass Reinforced is very low. Recommended printing parameters: 215 0C nozzle, 60 0C bed. If you are printing continuously in bigger quantities (above 1-2 kg), hard nozzles are recommended, in this case the printing parameters should be adjusted accordingly. Direct drive is recommended.